Casström Woodsman Curly Birch. Roger Harrington Design
Woodsman Curly Birch. Roger Harrington Design
Woodsman Curly Birch. Roger Harrington Design
Woodsman Curly Birch. Roger Harrington Design

Casström Woodsman Curly Birch. Roger Harrington Design (10804)

Marka : Casström
Fiyat : ₺1.300,77(KDV Dahil)
₺216,79 'den başlayan taksitlerle

Curly Birch, 9cm K720 (carbon) blade/Scandi grind 

  • Blade lengthApprox. 8,8 cm
  • Blade thicknessApprox. 4 mm
  • Blade widthApprox. 2,7 cm
  • BrandCasstrom
  • GrindScandi grind
  • HandleCurly Birch with black liners
  • Hardness58-60 HRC
  • SheathDeep pocket sheath in sturdy veg. tanned leather
  • SteelHigh carbon tool steel Böhler K720
  • Total lengthApprox. 20.5 cm
  • WeightApprox. 156g



Article no.: 10804


Proper full-tang knife with a blade measuring approx. 9cm long , straight and fairly round handle made to suit both large and small hands. The leather cord for the handle and a strong deep pocket leather sheath is included.

The blade is made of around 4mm thick Böhler K720 high carbon tool steel to make the blade extremely durable for heavy use such as log-splitting, or so-called "batoning" without making the knife to heavy or uncomfortable to carry.
The knife has a Scandinavian grind to make it very robust at the same time easy to carve wood with and easy to sharpen on a small flat whetstone/sharpener in the forest. The knife is a really good all-round tool for field use.

About the designer :
Roger Harrington is an experienced outdoorsman and knife maker who has taught Bushcraft and survival to civil and military customers for the last twenty years with his company Bison Bushcraft in Sussex , England.

About K720 steel:

Böhler Tool Steel K720 is a very tough and strong oil hardened high carbon tool steel. The chemical composition allows it to be hardened to a high degree whilst maintaining ductility and toughness at the same time as it is easy to sharpen and can obtain a razor sharp edge. Whilst easy to sharpen, the low chromium content means it will tarnish if left wet and it must therefore be wiped after use and protected by oil or wax when put away for storage.
Composition: C. 0.9%, Si. 0.25%, Mn. 2.0%, Cr. 0.35% V. 0.1% (HRC 58-60)